- 拉伸強度 [MPa]: 21.35
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 21.35 MPa | 3097 psi | |
| Elongation at Yield | 585 % | 585 % | |
| 100% Modulus | 0.00249 GPa | 0.361 ksi | |
| 200% Modulus | 0.00445 GPa | 0.646 ksi | |
| 300% Modulus | 0.00654 GPa | 0.949 ksi | |
| Tear Strength | 49.7 kN/m | 284 pli | |
| Taber Abrasion, mg/1000 Cycles | 30 @Load 1.00 kg | 30 @Load 2.20 lb | H-18 wheel |
| Compression Set | 47.1 % @Temperature 70.0 °C, Time 79200 sec | 47.1 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |