- 拉伸強(qiáng)度 [MPa]: 7.398
- 透光率 [%]: 90.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 46 | 46 | |
| Tensile Strength, Yield | 7.398 MPa | 1073 psi | |
| Elongation at Yield | 530 % | 530 % | |
| 100% Modulus | 0.000972 GPa | 0.141 ksi | |
| 200% Modulus | 0.00130 GPa | 0.189 ksi | |
| 300% Modulus | 0.00170 GPa | 0.247 ksi | |
| Tear Strength | 12.1 kN/m | 69.0 pli | Die C |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 149 °C | 0.167 hour @Temperature 300 °F | |