- 拉伸強度 [MPa]: 25.2
- 透光率 [%]: 90.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 66 | 66 | |
| Tensile Strength, Yield | 25.2 MPa | 3650 psi | |
| Elongation at Yield | 633 % | 633 % | |
| 100% Modulus | 0.00162 GPa | 0.235 ksi | |
| 200% Modulus | 0.00214 GPa | 0.310 ksi | |
| 300% Modulus | 0.00331 GPa | 0.480 ksi | |
| Tear Strength | 32.9 kN/m | 188 pli | Die C |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Cure Time | 8.00 min @Temperature 149 °C | 0.133 hour @Temperature 300 °F | |