- 拉伸強度 [MPa]: 34.8
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Mooney Viscosity | 57 @Temperature 100 °C | 57 @Temperature 212 °F | MS 1+10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 67 | 67 | |||
| Tensile Strength, Yield | 34.8 MPa | 5050 psi | |||
| Elongation at Break | 570 % | 570 % | |||
| 300% Modulus | 0.0128 GPa | 1.85 ksi | |||
| Tear Strength | 65.6 kN/m | 374 pli | Die C; ASTM D624 | ||
| Abrasion | 355 | 355 | NBS Index | ||
| Compression Set | 22 % @Temperature 70.0 °C, Time 79200 sec | 22 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 142 °C | 1.00 hour @Temperature 287 °F | |||
| Descriptive Properties | |||||
| Mooney Scorch | >= 39 | at 250oF; 43 minutes to 10 point rise | |||