- 拉伸強(qiáng)度 [MPa]: 6.55
- 透光率 [%]: 90.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 55 | 55 | |
| Tensile Strength, Yield | 6.55 MPa | 950 psi | |
| Elongation at Yield | 453 % | 453 % | |
| 100% Modulus | 0.00121 GPa | 0.175 ksi | |
| 200% Modulus | 0.00159 GPa | 0.230 ksi | |
| 300% Modulus | 0.00221 GPa | 0.320 ksi | |
| Tear Strength | 23.9 kN/m | 136 pli | Die C |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Cure Time | 7.00 min @Temperature 149 °C | 0.117 hour @Temperature 300 °F | |