- 拉伸強度 [MPa]: 20.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 20.90 MPa | 3032 psi | |
| Elongation at Yield | 629 % | 629 % | |
| 100% Modulus | 0.00214 GPa | 0.310 ksi | |
| 200% Modulus | 0.00441 GPa | 0.639 ksi | |
| 300% Modulus | 0.007894 GPa | 1.145 ksi | |
| Tear Strength | 54.1 kN/m | 309 pli | |
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg | 8.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 53.9 % @Temperature 70.0 °C, Time 79200 sec | 53.9 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 11.0 min @Temperature 154 °C | 0.183 hour @Temperature 309 °F | |