- 拉伸強(qiáng)度 [MPa]: 22.24
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 55 | 55 | |
| Tensile Strength, Yield | 22.24 MPa | 3226 psi | |
| Elongation at Yield | 654 % | 654 % | |
| 100% Modulus | 0.00201 GPa | 0.291 ksi | |
| 200% Modulus | 0.00300 GPa | 0.435 ksi | |
| 300% Modulus | 0.00421 GPa | 0.610 ksi | |
| Tear Strength | 36.6 kN/m | 209 pli | |
| Taber Abrasion, mg/1000 Cycles | 27 @Load 1.00 kg | 27 @Load 2.20 lb | H-18 wheel |
| Compression Set | 59.2 % @Temperature 70.0 °C, Time 79200 sec | 59.2 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 15.0 min @Temperature 155 °C | 0.250 hour @Temperature 311 °F | |