| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |
| Tensile Strength, Yield | 30.54 MPa | 4429 psi | |
| Elongation at Yield | 722 % | 722 % | |
| 100% Modulus | 0.00148 GPa | 0.214 ksi | |
| 200% Modulus | 0.00250 GPa | 0.363 ksi | |
| 300% Modulus | 0.00423 GPa | 0.613 ksi | |
| Tear Strength | 52.4 kN/m | 299 pli | |
| Taber Abrasion, mg/1000 Cycles | 12 @Load 1.00 kg | 12 @Load 2.20 lb | H-18 wheel |
| Compression Set | 55.6 % @Temperature 70.0 °C, Time 79200 sec | 55.6 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |