- 拉伸強度 [MPa]: 20.47
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 63 | 63 | |
| Tensile Strength, Yield | 20.47 MPa | 2969 psi | |
| Elongation at Yield | 720 % | 720 % | |
| 100% Modulus | 0.00157 GPa | 0.227 ksi | |
| 200% Modulus | 0.00288 GPa | 0.417 ksi | |
| 300% Modulus | 0.00463 GPa | 0.671 ksi | |
| Tear Strength | 57.8 kN/m | 330 pli | |
| Taber Abrasion, mg/1000 Cycles | 19 @Load 1.00 kg | 19 @Load 2.20 lb | H-18 wheel |
| Compression Set | 82.6 % @Temperature 70.0 °C, Time 79200 sec | 82.6 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 25.0 min @Temperature 149 °C | 0.417 hour @Temperature 300 °F | |