- 拉伸強度 [MPa]: 19.5
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |
| Tensile Strength, Yield | 19.50 MPa | 2828 psi | |
| Elongation at Yield | 523 % | 523 % | |
| 100% Modulus | 0.00457 GPa | 0.663 ksi | |
| 200% Modulus | 0.009156 GPa | 1.328 ksi | |
| 300% Modulus | 0.01333 GPa | 1.933 ksi | |
| Tear Strength | 59.8 kN/m | 341 pli | |
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg | 8.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 62.7 % @Temperature 70.0 °C, Time 79200 sec | 62.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 11.0 min @Temperature 154 °C | 0.183 hour @Temperature 309 °F | |