- 拉伸強度 [MPa]: 23.67
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 75 | 75 | |
| Tensile Strength, Yield | 23.67 MPa | 3433 psi | |
| Elongation at Yield | 490 % | 490 % | |
| 100% Modulus | 0.00459 GPa | 0.666 ksi | |
| 200% Modulus | 0.009915 GPa | 1.438 ksi | |
| 300% Modulus | 0.01623 GPa | 2.354 ksi | |
| Tear Strength | 60.6 kN/m | 346 pli | |
| Taber Abrasion, mg/1000 Cycles | 4.0 @Load 1.00 kg | 4.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 43.3 % @Temperature 70.0 °C, Time 79200 sec | 43.3 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 154 °C | 0.167 hour @Temperature 309 °F | |