- 拉伸強度 [MPa]: 13.4
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 77 | 77 | |
| Tensile Strength, Yield | 13.4 MPa | 1950 psi | |
| Elongation at Yield | 640 % | 640 % | |
| 100% Modulus | 0.00221 GPa | 0.321 ksi | |
| 200% Modulus | 0.00357 GPa | 0.518 ksi | |
| 300% Modulus | 0.00525 GPa | 0.762 ksi | |
| Tear Strength | 59.5 kN/m | 340 pli | |
| Taber Abrasion, mg/1000 Cycles | 23 @Load 1.00 kg | 23 @Load 2.20 lb | H-18 wheel |
| Compression Set | 91 % @Temperature 70.0 °C, Time 79200 sec | 91 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 25.0 min @Temperature 149 °C | 0.417 hour @Temperature 300 °F | |