- 拉伸強(qiáng)度 [MPa]: 21.15
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | |
| Tensile Strength, Yield | 21.15 MPa | 3067 psi | |
| Elongation at Yield | 331 % | 331 % | |
| 100% Modulus | 0.01097 GPa | 1.591 ksi | |
| 200% Modulus | 0.01789 GPa | 2.595 ksi | |
| 300% Modulus | 0.02056 GPa | 2.982 ksi | |
| Tear Strength | 66.0 kN/m | 377 pli | |
| Taber Abrasion, mg/1000 Cycles | 7.0 @Load 1.00 kg | 7.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 46.7 % @Temperature 70.0 °C, Time 79200 sec | 46.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 154 °C | 0.167 hour @Temperature 309 °F | |