- 拉伸強度 [MPa]: 32.53
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 57 | 57 | |
| Tensile Strength, Yield | 32.53 MPa | 4718 psi | |
| Elongation at Yield | 699 % | 699 % | |
| 100% Modulus | 0.00135 GPa | 0.196 ksi | |
| 200% Modulus | 0.00230 GPa | 0.333 ksi | |
| 300% Modulus | 0.00379 GPa | 0.549 ksi | |
| Tear Strength | 44.7 kN/m | 255 pli | |
| Taber Abrasion, mg/1000 Cycles | 5.0 @Load 1.00 kg | 5.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 50.8 % @Temperature 70.0 °C, Time 79200 sec | 50.8 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |