- 拉伸強度 [MPa]: 21.5
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 82 | 82 | |
| Tensile Strength, Yield | 21.50 MPa | 3118 psi | |
| Elongation at Yield | 481 % | 481 % | |
| 100% Modulus | 0.00574 GPa | 0.832 ksi | |
| 200% Modulus | 0.0117 GPa | 1.69 ksi | |
| 300% Modulus | 0.01612 GPa | 2.338 ksi | |
| Tear Strength | 63.4 kN/m | 362 pli | |
| Taber Abrasion, mg/1000 Cycles | 8.0 @Load 1.00 kg | 8.0 @Load 2.20 lb | H-18 wheel |
| Compression Set | 54.9 % @Temperature 70.0 °C, Time 79200 sec | 54.9 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 11.0 min @Temperature 154 °C | 0.183 hour @Temperature 309 °F | |