- 拉伸強度 [MPa]: 25.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 80 | 80 | |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | |
| Elongation at Yield | 683 % | 683 % | |
| 100% Modulus | 0.00229 GPa | 0.332 ksi | |
| 200% Modulus | 0.00442 GPa | 0.641 ksi | |
| 300% Modulus | 0.007460 GPa | 1.082 ksi | |
| Tear Strength | 85.5 kN/m | 488 pli | |
| Taber Abrasion, mg/1000 Cycles | 18 @Load 1.00 kg | 18 @Load 2.20 lb | H-18 wheel |
| Compression Set | 59.9 % @Temperature 70.0 °C, Time 79200 sec | 59.9 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |