- 拉伸強度 [MPa]: 21.75
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 58 | 58 | |
| Tensile Strength, Yield | 21.75 MPa | 3154 psi | |
| Elongation at Yield | 547 % | 547 % | |
| 100% Modulus | 0.00259 GPa | 0.376 ksi | |
| 200% Modulus | 0.00665 GPa | 0.964 ksi | |
| 300% Modulus | 0.01176 GPa | 1.705 ksi | |
| Tear Strength | 64.1 kN/m | 366 pli | |
| Taber Abrasion, mg/1000 Cycles | 11 @Load 1.00 kg | 11 @Load 2.20 lb | H-18 wheel |
| Compression Set | 53.8 % @Temperature 70.0 °C, Time 79200 sec | 53.8 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 11.0 min @Temperature 154 °C | 0.183 hour @Temperature 309 °F | |