- 拉伸強度 [MPa]: 19.06
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |
| Tensile Strength, Yield | 19.06 MPa | 2765 psi | |
| Elongation at Yield | 450 % | 450 % | |
| 100% Modulus | 0.00399 GPa | 0.578 ksi | |
| 200% Modulus | 0.009701 GPa | 1.407 ksi | |
| 300% Modulus | 0.01449 GPa | 2.102 ksi | |
| Tear Strength | 61.8 kN/m | 353 pli | |
| Taber Abrasion, mg/1000 Cycles | 12 @Load 1.00 kg | 12 @Load 2.20 lb | H-18 wheel |
| Compression Set | 70.3 % @Temperature 70.0 °C, Time 79200 sec | 70.3 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 11.0 min @Temperature 154 °C | 0.183 hour @Temperature 309 °F | |