- 拉伸強度 [MPa]: 26.1
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 | 50 | |
| Tensile Strength, Yield | 26.1 MPa | 3780 psi | |
| Elongation at Yield | 750 % | 750 % | |
| 100% Modulus | 0.00119 GPa | 0.172 ksi | |
| 200% Modulus | 0.00201 GPa | 0.292 ksi | |
| 300% Modulus | 0.00327 GPa | 0.474 ksi | |
| Tear Strength | 4.30 kN/m | 24.5 pli | |
| Taber Abrasion, mg/1000 Cycles | 13 @Load 1.00 kg | 13 @Load 2.20 lb | H-18 wheel |
| Compression Set | 64.2 % @Temperature 70.0 °C, Time 79200 sec | 64.2 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 25.0 min @Temperature 149 °C | 0.417 hour @Temperature 300 °F | |