- 拉伸強度 [MPa]: 14.4
- 透光率 [%]: 90.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 58 | 58 | |
| Tensile Strength, Yield | 14.4 MPa | 2090 psi | |
| Elongation at Yield | 506 % | 506 % | |
| 100% Modulus | 0.00138 GPa | 0.200 ksi | |
| 200% Modulus | 0.00190 GPa | 0.275 ksi | |
| 300% Modulus | 0.00279 GPa | 0.405 ksi | |
| Tear Strength | 25.9 kN/m | 148 pli | Die C |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Cure Time | 7.00 min @Temperature 149 °C | 0.117 hour @Temperature 300 °F | |