- 拉伸強度 [MPa]: 26.55
- 透光率 [%]: 90.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 26.55 MPa | 3851 psi | |
| Elongation at Yield | 462 % | 462 % | |
| 100% Modulus | 0.00234 GPa | 0.339 ksi | |
| 200% Modulus | 0.00506 GPa | 0.734 ksi | |
| 300% Modulus | 0.009839 GPa | 1.427 ksi | |
| Tear Strength | 34.5 kN/m | 197 pli | Die C |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |
| Processing Properties | Metric | English | Comments |
| Cure Time | 6.00 min @Temperature 149 °C | 0.100 hour @Temperature 300 °F | |