- 拉伸強度 [MPa]: 20.12
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 60 | 60 | |
| Tensile Strength, Yield | 20.12 MPa | 2918 psi | |
| Elongation at Yield | 721 % | 721 % | |
| 100% Modulus | 0.00157 GPa | 0.228 ksi | |
| 200% Modulus | 0.00197 GPa | 0.285 ksi | |
| 300% Modulus | 0.00255 GPa | 0.370 ksi | |
| Tear Strength | 21.9 kN/m | 125 pli | |
| Taber Abrasion, mg/1000 Cycles | 41 @Load 1.00 kg | 41 @Load 2.20 lb | H-18 wheel |
| Compression Set | 52.7 % @Temperature 70.0 °C, Time 79200 sec | 52.7 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 10.0 min @Temperature 155 °C | 0.167 hour @Temperature 311 °F | |