- 拉伸強度 [MPa]: 34.5
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 75 | 75 | |||
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | |||
| Elongation at Yield | 630 % | 630 % | |||
| 100% Modulus | 0.00207 GPa | 0.300 ksi | |||
| 300% Modulus | 0.00724 GPa | 1.05 ksi | |||
| Tear Strength | 57.0 kN/m | 325 pli | Graves | ||
| Compression Set | 40 % @Temperature 70.0 °C, Time 79200 sec | 40 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 154 °C | 0.500 hour @Temperature 310 °F | |||
| Descriptive Properties | |||||
| 500% Modulus (ksi) | 2.6 | ||||
| Mooney Scorch | >= 56 | at 250oF; >30 minutes to a 10 point rise | |||