- 密度 [g/cm3]: 1.2
- 缺口沖擊強(qiáng)度: 0.46
- 斷裂伸長(zhǎng)率 [%]: 311
- 彎曲模量 [MPa]: 15.06
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.210 % | 0.210 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec | 0.0010 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec | 0.0070 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 209 MPa | 30300 psi | 5 mm/min; ISO 527 |
| 210 MPa | 30500 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ISO 527 |
| 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 19.33 GPa | 2804 ksi | 1 mm/min; ISO 527 |
| 19.42 GPa | 2817 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 300 MPa | 43500 psi | ISO 178 |
| 309 MPa | 44800 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 311 MPa | 45100 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 15.06 GPa | 2184 ksi | 2 mm/min; ISO 178 |
| 15.4 GPa | 2230 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.460 J/cm | 0.862 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.69 J/cm | 18.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m2 | 6.66 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 62.0 kJ/m2 | 29.5 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 22.0 J @Temperature 23.0 °C | 16.2 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 16.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 8.89 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 72.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 40.0 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 222 °C @Thickness 3.20 mm | 432 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 213 °C @Thickness 3.20 mm | 415 °F @Thickness 0.126 in | unannealed; ASTM D648 | |