- 密度 [g/cm3]: 1.31
- 缺口沖擊強度: 0.66
- 拉伸強度 [MPa]: 119.0
- 斷裂伸長率 [%]: 205
- 彎曲模量 [MPa]: 9.15
- 熱變形溫度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | ASTM D792 |
| 1.31 g/cc | 0.0473 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.270 % | 0.270 % | 50% RH, 24 hrs; ASTM D570 |
| 0.400 % | 0.400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec | 0.0040 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm @Time 86400 sec | 0.0070 - 0.010 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 119 MPa | 17300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 119 MPa | 17300 psi | Type I, 5 mm/min; ASTM D638 |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 |
| 2.5 % | 2.5 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 13.43 GPa | 1948 ksi | 1 mm/min; ISO 527 |
| 23.18 GPa | 3362 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 214 MPa | 31000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 205 MPa | 29700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 9.15 GPa | 1330 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.81 GPa | 1420 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.660 J/cm | 1.24 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.18 J/cm | 13.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m2 | 19.0 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ASTM D257 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 219 °C @Thickness 3.20 mm | 426 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 444 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 201 °C @Thickness 3.20 mm | 394 °F @Thickness 0.126 in | unannealed; ASTM D648 | |