- 密度 [g/cm3]: 1.42
- 缺口沖擊強度: 1.76
- 彎曲模量 [MPa]: 9.03
- 熱變形溫度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in3 | ASTM D792 |
| 1.42 g/cc | 0.0513 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.180 % | 0.180 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec | 0.0010 in/in @Time 24.0 hour | ASTM D955 |
| 0.0015 cm/cm @Time 86400 sec | 0.0015 in/in @Time 24.0 hour | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec | 0.0070 in/in @Time 24.0 hour | ASTM D955 |
| 0.0073 cm/cm @Time 86400 sec | 0.0073 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 183 MPa | 26500 psi | ISO 527 |
| 192 MPa | 27800 psi | ASTM D638 | |
| Elongation at Break | 3.4 % | 3.4 % | ISO 527 |
| 3.5 % | 3.5 % | ASTM D638 | |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 1 mm/min; ISO 527 |
| 11.92 GPa | 1729 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 273 MPa | 39600 psi | ISO 178 |
| 282 MPa | 40900 psi | ASTM D790 | |
| Flexural Modulus | 9.03 GPa | 1310 ksi | ASTM D790 |
| 9.80 GPa | 1420 ksi | ISO 178 | |
| Izod Impact, Notched | 1.76 J/cm | 3.30 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.72 J/cm | 25.70 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m2 | 7.61 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 88.0 kJ/m2 | 41.9 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 43.2 μm/m-°C @Temperature -40.0 - 40.0 °C | 24.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 44.8 μm/m-°C @Temperature -40.0 - 40.0 °C | 24.9 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 59.4 μm/m-°C @Temperature -40.0 - 40.0 °C | 33.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 59.8 μm/m-°C @Temperature -40.0 - 40.0 °C | 33.2 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C @Thickness 3.20 mm | 432 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 214 °C @Thickness 3.20 mm | 417 °F @Thickness 0.126 in | unannealed; ASTM D648 | |