- 密度 [g/cm3]: 1.46
- 缺口沖擊強度: 1.17
- 彎曲模量 [MPa]: 8.48
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in3 | ASTM D792 |
| 1.46 g/cc | 0.0527 lb/in3 | ISO 1183 | |
| Moisture Absorption | 0.130 % | 0.130 % | 50% RH, 24 hrs; ASTM D570 |
| 0.220 % | 0.220 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm @Time 86400 sec | 0.0017 in/in @Time 24.0 hour | ISO 294 |
| 0.0020 cm/cm @Time 86400 sec | 0.0020 in/in @Time 24.0 hour | ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Time 86400 sec | 0.0070 in/in @Time 24.0 hour | ASTM D955 |
| 0.0070 cm/cm @Time 86400 sec | 0.0070 in/in @Time 24.0 hour | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 149 MPa | 21600 psi | ASTM D638 |
| 150 MPa | 21800 psi | ISO 527 | |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| 2.6 % | 2.6 % | ISO 527 | |
| Tensile Modulus | 9.80 GPa | 1420 ksi | 1 mm/min; ISO 527 |
| 11.03 GPa | 1600 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 221 MPa | 32100 psi | ASTM D790 |
| 228 MPa | 33100 psi | ISO 178 | |
| Flexural Modulus | 8.48 GPa | 1230 ksi | ASTM D790 |
| 9.70 GPa | 1410 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.39 J/cm | 17.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 | 5.71 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m2 | 30.9 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.70 | 0.70 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm3/N-M | 15.0 x 10-10 in3-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 28.8 μm/m-°C @Temperature -40.0 - 40.0 °C | 16.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 29.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 16.1 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 73.8 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| 74.9 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.6 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C @Thickness 3.20 mm | 433 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 211 °C | 412 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 216 °C @Thickness 3.20 mm | 421 °F @Thickness 0.126 in | unannealed; ASTM D648 | |