- 密度 [g/cm3]: 1.24
- 缺口沖擊強度: 1.04
- 斷裂伸長率 [%]: 326
- 彎曲模量 [MPa]: 16.1
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Density | 1.24 g/cc | 0.0448 lb/in3 | ASTM D792 |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Time 86400 sec | 0.0010 - 0.0030 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec | 0.0080 - 0.010 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 214 MPa | 31000 psi | Type I, 5 mm/min; ASTM D638 |
| 243 MPa | 35200 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | 5 mm/min; ISO 527 |
| 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 23.01 GPa | 3337 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 325 MPa | 47100 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| 349 MPa | 50600 psi | ISO 178 | |
| Flexural Yield Strength | 326 MPa | 47300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 16.1 GPa | 2340 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 18.77 GPa | 2722 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.04 J/cm | 1.95 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.20 J/cm | 17.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 | 5.71 ft-lb/in2 | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 59.0 kJ/m2 | 28.1 ft-lb/in2 | 80*10*4; ISO 180/1U |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 12.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 6.67 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| CTE, linear, Transverse to Flow | 55.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 30.6 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 220 °C @Thickness 3.20 mm | 428 °F @Thickness 0.126 in | unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 211 °C @Thickness 3.20 mm | 412 °F @Thickness 0.126 in | unannealed; ASTM D648 | |