- 密度 [g/cm3]: 1.44
- 缺口沖擊強度: 0.9
- 彎曲模量 [MPa]: 8.61
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec | 0.0020 in/in @Time 24.0 hour | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Time 86400 sec | 0.0090 in/in @Time 24.0 hour | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 136 MPa | 19700 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 212 MPa | 30700 psi | ASTM D790 |
| Flexural Modulus | 8.61 GPa | 1250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.07 J/cm | 17.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 201 °C @Thickness 3.20 mm | 394 °F @Thickness 0.126 in | unannealed; ASTM D648 |