- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 2.0
- 彎曲強度 [MPa]: 130.0
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | |
| Water Absorption | 2.0 % | 2.0 % | |
| Melt Flow | 10 g/10 min | 10 g/10 min | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 130 MPa | 18900 psi | |
| Elongation at Break | 5.0 % | 5.0 % | |
| Modulus of Elasticity | 5.50 GPa | 798 ksi | |
| Charpy Impact Unnotched | 8.00 J/cm2 | 38.1 ft-lb/in2 | |
| 2.00 J/cm2 @Temperature -30.0 °C | 9.52 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.20 J/cm2 | 5.71 ft-lb/in2 | |
| 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | |
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | ||
| Dielectric Strength | 38.0 kV/mm | 965 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | <= 50.0 μm/m-°C @Temperature 20.0 °C | <= 27.8 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | |
| Vicat Softening Point | 205 °C | 401 °F | 50°C/hr/50 N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||