- 缺口沖擊強度: 1.12
- 拉伸強度 [MPa]: 193.0
- 彎曲模量 [MPa]: 15.34
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 193 MPa | 28000 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 24.1 GPa | 3500 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 286 MPa | 41500 psi | ASTM D790 |
| Flexural Modulus | 15.34 GPa | 2225 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 2.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | Unannealed; ASTM D648 |