- 吸水率 [%]: 0.35
- 缺口沖擊強度: 0.694
- 拉伸強度 [MPa]: 89.6
- 彎曲模量 [MPa]: 4.48
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.135 g/cc | 1.135 g/cc | ASTM D792 |
| Water Absorption | 0.35 % @Thickness 3.17 mm | 0.35 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0055 cm/cm | 0.0050 - 0.0055 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 89.6 MPa | 13000 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 4.48 GPa | 650 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 138 MPa | 20000 psi | ASTM D790 |
| Flexural Modulus | 4.48 GPa | 650 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 1.30 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |