- 吸水率 [%]: 0.2
- 缺口沖擊強(qiáng)度: 0.53
- 彎曲模量 [MPa]: 5.17
- 熱變形溫度 [℃]: 206.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 | ||
| Water Absorption | 0.20 % | 0.20 % | @ 24 hrs; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0050 cm/cm @Thickness 3.18 mm | 0.0040 - 0.0050 in/in @Thickness 0.125 in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 | ||
| Tensile Modulus | 6.21 GPa | 901 ksi | 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 179 MPa | 26000 psi | 1.3 mm/min; ASTM D790 | ||
| Flexural Modulus | 5.17 GPa | 750 ksi | 1.3 mm/min; ASTM D790 | ||
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | Injection Molded; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 206 °C | 403 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | Unannealed; ASTM D648 | ||
| Descriptive Properties | |||||
| Features | Good Chemical Resistance | ||||
| Good Stability | |||||
| Low to No Water Absorption | |||||
| Semi Crystalline | |||||
| Filler / Reinforcement | Glass Fiber Reinforcement, 20% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | Nylon 612 | ||||
| Generic Name | Polyamide 612 (Nylon 612) | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Uses | Aerospace Applications | ||||
| Appliance Components | |||||
| Automotive Applications | |||||
| Electrical/Electronic Applications | |||||
| Housings | |||||
| Industrial Applications | |||||
| Marine Applications | |||||
| Sporting Goods | |||||