- 吸水率 [%]: 0.15
- 缺口沖擊強度: 1.44
- 彎曲強度 [MPa]: 159.0
- 彎曲模量 [MPa]: 8.96
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 | ||
| Water Absorption | 0.15 % | 0.15 % | 24 hr. Immersion; ASTM D570 | ||
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 159 MPa | 23000 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 8.96 GPa | 1300 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 165 MPa | 24000 psi | ASTM D790 | ||
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.44 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 2.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | Annealed, 0.125 in bars; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 217 °C | 423 °F | Annealed, 0.125 in bars; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | Molding | ||
| Mold Temperature | 93.3 - 107 °C | 200 - 225 °F | |||
| Drying Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |||
| Dry Time | 2 hour | 2 hour | |||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.