| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ASTM D792 | ||
| Filler Content | 43 % | 43 % | |||
| Water Absorption | 0.20 % @Thickness 3.18 mm, Time 86400 sec | 0.20 % @Thickness 0.125 in, Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 171 MPa | 24800 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Elongation at Break | 3.5 % | 3.5 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 255 MPa | 37000 psi | ASTM D790 | ||
| Flexural Modulus | 10.3 GPa | 1490 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.28 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 2.40 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 215 °C | 419 °F | ASTM D789 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C @Thickness 3.18 mm | 410 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C @Thickness 3.18 mm | 392 °F @Thickness 0.125 in | Unannealed; ASTM D648 | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Forms | Pellets | ||||
| Generic Name | Polyamide 612 (Nylon 6/12) | ||||
| Regional Availability | North America | ||||
| South America | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.