- 密度 [g/cm3]: 1.45
- 吸水率 [%]: 0.15
- 缺口沖擊強(qiáng)度: 1.17
- 斷裂伸長(zhǎng)率 [%]: 165
- 彎曲強(qiáng)度 [MPa]: 159.0
- 彎曲模量 [MPa]: 9.00
- 熱變形溫度 [℃]: 223.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.0010 - 0.0020 cm/cm @Thickness 3.17 mm | 0.0010 - 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 159 MPa | 23100 psi | ASTM D638 |
| Elongation at Break | 1.0 - 3.0 % | 1.0 - 3.0 % | ASTM D638 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ASTM D638 |
| Flexural Yield Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 - 1.44 J/cm @Thickness 6.35 mm | 2.19 - 2.70 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 223 °C | 433 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 217 °C | 423 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 271 - 293 °C | 520 - 559 °F | Stock |
| Mold Temperature | 93.0 - 107 °C | 199 - 225 °F | |
| Drying Temperature | 82.0 - 93.0 °C | 180 - 199 °F | |