- 密度 [g/cm3]: 1.16
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.43
- 彎曲強度 [MPa]: 52.0
- 硬度: 113.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hrs. ASTM D570 |
| Linear Mold Shrinkage | 0.012 cm/cm @Thickness 3.17 mm | 0.012 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Ultimate | 52.0 MPa | 7540 psi | ASTM D638 |
| Elongation at Break | 7.0 - 10 % | 7.0 - 10 % | ASTM D638 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ASTM D638 |
| Izod Impact, Notched | 0.430 J/cm @Thickness 6.35 mm | 0.806 ft-lb/in @Thickness 0.250 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 249 - 271 °C | 480 - 520 °F | Stock |
| Mold Temperature | 49.0 - 82.0 °C | 120 - 180 °F | |
| Drying Temperature | 82.0 °C | 180 °F | |