- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 1.01
- 拉伸強度 [MPa]: 53.0
- 彎曲模量 [MPa]: 1.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ISO 1183 |
| Water Absorption | 1.01 % | 1.01 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2/1A |
| Tensile Modulus | 1.70 GPa | 247 ksi | ISO 527-1/-2 |
| Flexural Modulus | 1.80 GPa | 261 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.900 J/cm2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | ISO 11357 |