- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 1.01
- 拉伸強(qiáng)度 [MPa]: 63.0
- 彎曲模量 [MPa]: 2.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | ISO 1183 |
| Water Absorption | 1.01 % | 1.01 % | ISO 62 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | ISO 527-1/-2 |
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-2/1A |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1/-2 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/2 |