- 吸水率 [%]: 0.2
- 缺口沖擊強度: 1.28
- 拉伸強度 [MPa]: 162.0
- 彎曲模量 [MPa]: 9.51
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Thickness 3.17 mm | 0.20 % @Thickness 0.125 in | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 162 MPa | 23500 psi | Type 1 - Rigids, Break, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Modulus | 9.51 GPa | 1380 ksi | ASTM D790 |
| Izod Impact, Notched | 1.28 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 2.40 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 215 °C | 419 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | Unannealed; ASTM D648 |