- 缺口沖擊強(qiáng)度: 0.374
- 拉伸強(qiáng)度 [MPa]: 51.7
- 斷裂伸長(zhǎng)率 [%]: 55.2
- 彎曲模量 [MPa]: 1.72
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Filler Content | 0.00 % | 0.00 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 |
| Elongation at Yield | 75 % | 75 % | ASTM D638 |
| Flexural Yield Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.374 J/cm @Temperature 22.8 °C | 0.700 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C | 170 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 243 - 271 °C | 470 - 520 °F | |
| Mold Temperature | 65.6 - 79.4 °C | 150 - 175 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C | 2 - 4 hour @Temperature 175 °F | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.172 - 0.517 MPa | 25.0 - 75.0 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm | |
- 關(guān)鍵詞:
- 供應(yīng)
- Lubricated
- PA612
- Clariant Renol 612-01L Nylon 612