- 密度 [g/cm3]: 1.07
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.43
- 拉伸強度 [MPa]: 53.0
- 彎曲模量 [MPa]: 1.50
- 硬度: 120.0
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | DAM; ASTM D792 | ||
| Density | 1.07 g/cc | 0.0387 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 0.30 % @Temperature 23.0 °C | 0.30 % @Temperature 73.4 °F | Immersion 24h; DAM; ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 120 | 120 | DAM; ASTM D785 | ||
| Tensile Strength | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 60.0 MPa @Temperature 23.0 °C | 8700 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Tensile Strength, Yield | 53.0 MPa @Temperature 23.0 °C | 7690 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 65.0 MPa @Temperature 23.0 °C | 9430 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 22 % @Temperature 23.0 °C | 22 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 30 % @Temperature 23.0 °C | 30 % @Temperature 73.4 °F | DAM; ASTM D638 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| 75 % @Temperature 23.0 °C | 75 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| Elongation at Yield | 4.4 % @Temperature 23.0 °C | 4.4 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 18 % @Temperature 23.0 °C | 18 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.50 GPa @Temperature 23.0 °C | 218 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 2.50 GPa @Temperature 23.0 °C | 363 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Strength | 44.0 MPa @Temperature 23.0 °C | 6380 psi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 80.0 MPa @Temperature 23.0 °C | 11600 psi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Flexural Modulus | 1.50 GPa @Temperature 23.0 °C | 218 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 1.50 GPa @Temperature 23.0 °C | 218 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | |||
| 2.18 GPa @Temperature 23.0 °C | 316 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| 2.30 GPa @Temperature 23.0 °C | 334 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Izod Impact, Notched | 0.430 J/cm @Temperature 23.0 °C | 0.806 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| 0.480 J/cm @Temperature 23.0 °C | 0.899 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
| Izod Impact, Notched (ISO) | 4.00 kJ/m2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature 23.0 °C | 1.90 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 218 °C | 424 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | DAM; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | DAM; ASTM D648 | ||
| 62.0 °C | 144 °F | DAM; ISO 75-1/-2 | |||
| UL RTI, Electrical | 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 105 °C @Thickness 0.860 mm | 221 °F @Thickness 0.0339 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 0.860 mm | 149 °F @Thickness 0.0339 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| 65.0 °C @Thickness 0.860 mm | 149 °F @Thickness 0.0339 in | DAM; UL 746B | |||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.860 mm | HB @Thickness 0.0339 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 0.860 mm | HB @Thickness 0.0339 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 218 °C | 424 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 250 °C | 482 °F | DAM; Optimum | |||
| 230 - 290 °C | 446 - 554 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Carbon Black | DAM | |||
| Heat Stabilizer | DAM | ||||
| Lubricant | DAM | ||||
| Appearance | Black Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Extrudable - Blown Film | Yes | DAM | |||
| Extrudable - Coating | Yes | DAM | |||
| Extrudable - Filament | Yes | DAM | |||
| Extrudable - Hose | Yes | DAM | |||
| Extrudable - Sheet | Yes | DAM | |||
| Extrudable - Tubing | Yes | DAM | |||
| Extrudable - Wire and Cable | Yes | DAM | |||
| Extrusion Blow Moldable | Yes | DAM | |||
| Features | Chemical Resistance, Good | DAM | |||
| Heat Aging Resistance, Good | DAM | ||||
| Lubricated | DAM | ||||
| Lubricated | DAM | ||||
| Wear Resistance, Good | DAM | ||||
| Weather Resistance, Good | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 612 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Injection Blow Moldable | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA612< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA612 | DAM | |||
| Processing Method | Extrusion | DAM | |||
| Injection Molding | DAM | ||||
| Product Category | Extrusion Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| UV Resistant/Weatherable Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA612 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Automotive Applications | DAM | |||