- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 0.08
- 缺口沖擊強度: 0.427
- 拉伸強度 [MPa]: 108.0
- 斷裂伸長率 [%]: 138
- 彎曲強度 [MPa]: 96.5
- 彎曲模量 [MPa]: 5.52
- 硬度: 106.0
- 熱變形溫度 [℃]: 144.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 - 1.55 g/cc | 0.0394 - 0.0560 lb/in3 | Average value: 1.28 g/cc Grade Count:34 |
| Filler Content | 8.00 - 40.0 % | 8.00 - 40.0 % | Average value: 22.3 % Grade Count:24 |
| Water Absorption | 0.0800 - 0.300 % | 0.0800 - 0.300 % | Average value: 0.183 % Grade Count:22 |
| Additive Loading | 20.0 - 30.0 % | 20.0 - 30.0 % | Average value: 26.7 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000500 - 0.00600 cm/cm | 0.000500 - 0.00600 in/in | Average value: 0.00216 cm/cm Grade Count:34 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.00900 cm/cm | 0.00200 - 0.00900 in/in | Average value: 0.00375 cm/cm Grade Count:14 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 - 120 | 106 - 120 | Average value: 117 Grade Count:12 |
| Tensile Strength, Ultimate | 96.5 - 231 MPa | 14000 - 33500 psi | Average value: 170 MPa Grade Count:30 |
| Tensile Strength, Yield | 108 - 200 MPa | 15700 - 29000 psi | Average value: 133 MPa Grade Count:4 |
| Elongation at Break | 1.00 - 5.00 % | 1.00 - 5.00 % | Average value: 2.71 % Grade Count:34 |
| Modulus of Elasticity | 6.55 - 27.6 GPa | 950 - 4000 ksi | Average value: 16.2 GPa Grade Count:27 |
| Flexural Yield Strength | 138 - 348 MPa | 20000 - 50500 psi | Average value: 251 MPa Grade Count:34 |
| Flexural Modulus | 5.52 - 22.4 GPa | 800 - 3250 ksi | Average value: 12.9 GPa Grade Count:34 |
| Izod Impact, Notched | 0.427 - 1.28 J/cm | 0.800 - 2.40 ft-lb/in | Average value: 0.843 J/cm Grade Count:34 |
| Izod Impact, Unnotched | 2.40 - 10.7 J/cm | 4.50 - 20.0 ft-lb/in | Average value: 6.27 J/cm Grade Count:31 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.100 - 1.00e+8 ohm-cm | 0.100 - 1.00e+8 ohm-cm | Average value: 3.88e+6 ohm-cm Grade Count:26 |
| Surface Resistance | 100 - 1.00e+10 ohm | 100 - 1.00e+10 ohm | Average value: 3.92e+8 ohm Grade Count:13 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 18.0 - 19.8 μm/m-°C | 10.0 - 11.0 μin/in-°F | Average value: 19.4 μm/m-°C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 144 - 221 °C | 292 - 430 °F | Average value: 205 °C Grade Count:19 |
| Deflection Temperature at 1.8 MPa (264 psi) | 139 - 227 °C | 283 - 440 °F | Average value: 206 °C Grade Count:31 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:27 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 252 - 279 °C | 485 - 535 °F | Average value: 266 °C Grade Count:17 |
| Melt Temperature | 249 - 285 °C | 480 - 545 °F | Average value: 267 °C Grade Count:10 |
| Mold Temperature | 60.0 - 93.3 °C | 140 - 200 °F | Average value: 76.7 °C Grade Count:27 |
| Drying Temperature | 79.4 °C | 175 °F | Average value: 79.4 °C Grade Count:10 |
| Dry Time | 4.00 hour | 4.00 hour | Average value: 4.00 hour Grade Count:7 |
| Moisture Content | 0.200 % | 0.200 % | Average value: 0.200 % Grade Count:10 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:10 |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi | Average value: 96.5 MPa Grade Count:27 |