- 密度 [g/cm3]: 1.03
- 缺口沖擊強(qiáng)度: 0.29
- 斷裂伸長率 [%]: 23.0
- 彎曲強(qiáng)度 [MPa]: 27.0
- 彎曲模量 [MPa]: 0.520
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 - 1.07 g/cc | 0.0372 - 0.0387 lb/in3 | Average value: 1.05 g/cc Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 27.0 - 33.0 MPa | 3920 - 4790 psi | Average value: 29.0 MPa Grade Count:3 |
| Elongation at Break | 41.0 - 300 % | 41.0 - 300 % | Average value: 214 % Grade Count:3 |
| Flexural Yield Strength | 23.0 - 52.0 MPa | 3340 - 7540 psi | Average value: 33.7 MPa Grade Count:3 |
| Flexural Modulus | 0.520 - 1.30 GPa | 75.4 - 189 ksi | Average value: 0.867 GPa Grade Count:3 |
| Izod Impact, Notched | 0.290 - 0.850 J/cm | 0.543 - 1.59 ft-lb/in | Average value: 0.647 J/cm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 135 - 215 °C | 275 - 419 °F | Average value: 162 °C Grade Count:3 |