- 密度 [g/cm3]: 1.08
- 拉伸強度 [MPa]: 82.0
- 彎曲模量 [MPa]: 2.70
- 熱變形溫度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | ISO 1183 |
| Viscosity Test | 160 cm3/g | 160 cm3/g | Viscosity Number; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 84 | 84 | ISO 868 |
| Ball Indentation Hardness | 130 MPa | 18900 psi | H30; ISO 2039-1 |
| Tensile Strength, Yield | 82.0 MPa | 11900 psi | 50 mm/min; ISO 527-1/2 |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527-1/2 |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min; ISO 527-1/2 |
| 8.0 % | 8.0 % | 5 mm/min, Outer fiber strain at maximum stress; ISO 178 | |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527-1/2 |
| Flexural Strength | 80.0 MPa | 11600 psi | 5 mm/min, at 3.5% Strain; ISO 178 |
| 118 MPa | 17100 psi | 5 mm/min; ISO 178 | |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 0.000 °C | NB @Temperature 32.0 °F | ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.900 J/cm2 @Temperature 23.0 °C | 4.28 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 800 MPa | 116000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| >= 1.00e+15 ohm | >= 1.00e+15 ohm | Spec.; IEC 60093 | |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.0425 @Frequency 1e+6 Hz | 0.0425 @Frequency 1e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A, 100 drops; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 70.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 μin/in-°F @Temperature 73.4 - 176 °F | Longitudinal; ISO 11359 |
| CTE, linear, Transverse to Flow | 70.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 38.9 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ISO 75-1/2 |
| Vicat Softening Point | 99.0 °C | 210 °F | 50N; ISO 306 |
| Glass Transition Temp, Tg | 93.0 °C | 199 °F | Tg, 10 K/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||