- 密度 [g/cm3]: 1.48
- 彎曲模量 [MPa]: 12.0
- 熱變形溫度 [℃]: 230.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in3 | ISO 1183 |
| Viscosity Test | 130 cm3/g | 130 cm3/g | Viscosity Number; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 90 | 90 | ISO 868 |
| Ball Indentation Hardness | 262 MPa | 38000 psi | H30; ISO 2039-1 |
| Tensile Strength at Break | 220 MPa | 31900 psi | 5 mm/min; ISO 527-1/2 |
| Elongation at Break | 3.2 % | 3.2 % | 5 mm/min; ISO 527-1/2 |
| 4.3 % | 4.3 % | 5 mm/min, Outer fiber strain at break; ISO 178 | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | ISO 527-1/2 |
| Flexural Strength | 302 MPa | 43800 psi | 5 mm/min, at 3.5% Strain; ISO 178 |
| 342 MPa | 49600 psi | 5 mm/min; ISO 178 | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 |
| Charpy Impact Unnotched | 8.00 J/cm2 @Temperature -30.0 °C | 38.1 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU |
| 8.70 J/cm2 @Temperature 0.000 °C | 41.4 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eU | |
| 9.60 J/cm2 @Temperature 23.0 °C | 45.7 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 1.10 J/cm2 @Temperature 0.000 °C | 5.24 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eA | |
| 1.40 J/cm2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 9600 MPa | 1.39e+6 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 5200 MPa | 754000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| >= 1.00e+15 ohm | >= 1.00e+15 ohm | Spec.; IEC 60093 | |
| Dielectric Constant | 6.2 @Frequency 1e+6 Hz | 6.2 @Frequency 1e+6 Hz | IEC 60250 |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.025 @Frequency 1e+6 Hz | 0.025 @Frequency 1e+6 Hz | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Test Solution A, 100 drops; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 22.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 12.2 μin/in-°F @Temperature 73.4 - 176 °F | Longitudinal; ISO 11359 |
| CTE, linear, Transverse to Flow | 38.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 21.1 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359 |
| Melting Point | 260 °C | 500 °F | 10 K/min; DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 230 °C | 446 °F | ISO 75-1/2 |
| Vicat Softening Point | 230 °C | 446 °F | 50N; ISO 306 |
| Glass Transition Temp, Tg | 93.0 °C | 199 °F | Tg, 10 K/min |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||