- 密度 [g/cm3]: 1.12
- 拉伸強度 [MPa]: 88.0
- 彎曲模量 [MPa]: 3.00
- 熱變形溫度 [℃]: 140.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ISO 1183 | ||
| Viscosity Test | 115 cm3/g | 115 cm3/g | Viscosity Number; ISO 307 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 | 86 | ISO 868 | ||
| Ball Indentation Hardness | 150 MPa | 21800 psi | H30; ISO 2039-1 | ||
| Tensile Strength, Yield | 88.0 MPa | 12800 psi | 50 mm/min; ISO 527-1/2 | ||
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527-1/2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1/2 | ||
| 9.0 % | 9.0 % | 5 mm/min, Outer fiber strain at maximum stress; ISO 178 | |||
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/2 | ||
| Flexural Strength | 84.0 MPa | 12200 psi | 5 mm/min, at 3.5% Strain; ISO 178 | ||
| 147 MPa | 21300 psi | 5 mm/min; ISO 178 | |||
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 | ||
| Charpy Impact Unnotched | NB @Temperature 0.000 °C | NB @Temperature 32.0 °F | ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 0.900 J/cm2 @Temperature 0.000 °C | 4.28 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eA | |||
| 1.00 J/cm2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 2200 MPa | 319000 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 1600 MPa | 232000 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 | ||
| >= 1.00e+15 ohm | >= 1.00e+15 ohm | Spec.; IEC 60093 | |||
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz | 3.8 @Frequency 1e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | K20/P50; IEC 60243-1 | ||
| Dissipation Factor | 0.028 @Frequency 1e+6 Hz | 0.028 @Frequency 1e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test Solution A, 100 drops; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 60.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 33.3 μin/in-°F @Temperature 73.4 - 176 °F | Longitudinal; ISO 11359 | ||
| CTE, linear, Transverse to Flow | 60.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 33.3 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75-1/2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1/2 | ||
| Vicat Softening Point | 140 °C | 284 °F | 50N; ISO 306 | ||
| Glass Transition Temp, Tg | 149 °C | 300 °F | Tg, 10 K/min | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.800 mm | 149 °F @Thickness 0.0315 in | UL 746 B | ||
| 65.0 °C @Thickness 1.60 mm | 149 °F @Thickness 0.0630 in | UL 746 B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 0.800 mm | 149 °F @Thickness 0.0315 in | UL 746 B | ||
| 65.0 °C @Thickness 1.60 mm | 149 °F @Thickness 0.0630 in | UL 746 B | |||
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |||
| V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | ||||
| Glow Wire Test | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | IEC 60695-2-1/0-3 | ||
| Optical Properties | Metric | English | Comments | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Descriptive Properties | |||||
| Color | Black | ||||