- 密度 [g/cm3]: 1.12
- 拉伸強(qiáng)度 [MPa]: 90.0
- 彎曲模量 [MPa]: 3.00
- 熱變形溫度 [℃]: 140.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ISO 1183 |
| Viscosity Test | 125 cm3/g | 125 cm3/g | Viscosity Number; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 86 | 86 | ISO 868 |
| Ball Indentation Hardness | 155 MPa | 22500 psi | H30; ISO 2039-1 |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50 mm/min; ISO 527-1/2 |
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; ISO 527-1/2 |
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1/2 |
| 8.5 % | 8.5 % | 5 mm/min, Outer fiber strain at maximum stress; ISO 178 | |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527-1/2 |
| Flexural Strength | 104 MPa | 15100 psi | 5 mm/min, at 3.5% Strain; ISO 178 |
| 152 MPa | 22000 psi | 5 mm/min; ISO 178 | |
| Flexural Modulus | 3.00 GPa | 435 ksi | ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 0.000 °C | NB @Temperature 32.0 °F | ISO 179/1eU |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA |
| 0.900 J/cm2 @Temperature 0.000 °C | 4.28 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eA | |
| 1.10 J/cm2 @Temperature 23.0 °C | 5.24 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 2500 MPa | 363000 psi | ISO 899-1 |
| Tensile Creep Modulus, 1000 hours | 1300 MPa | 189000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| >= 1.00e+15 ohm | >= 1.00e+15 ohm | Spec.; IEC 60093 | |
| Dielectric Constant | 3.7 @Frequency 1e+6 Hz | 3.7 @Frequency 1e+6 Hz | IEC 60250 |
| 4.0 @Frequency 50 Hz | 4.0 @Frequency 50 Hz | IEC 60250 | |
| 4.3 @Frequency 100 Hz | 4.3 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 26.0 kV/mm | 660 kV/in | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.018 @Frequency 50 Hz | 0.018 @Frequency 50 Hz | IEC 60250 |
| 0.026 @Frequency 1e+6 Hz | 0.026 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | Test Solution A, 100 drops; IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 53.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 29.4 μin/in-°F @Temperature 73.4 - 176 °F | Longitudinal; ISO 11359 |
| CTE, linear, Transverse to Flow | 54.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 30.0 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ISO 75-1/2 |
| Vicat Softening Point | 142 °C | 288 °F | 50N; ISO 306 |
| 148 °C | 298 °F | 10N; ISO 306 | |
| Glass Transition Temp, Tg | 150 °C | 302 °F | Tg, 10 K/min |
| UL RTI, Mechanical with Impact | 80.0 °C @Thickness 0.800 mm | 176 °F @Thickness 0.0315 in | UL 746 B |
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 0.800 mm | 185 °F @Thickness 0.0315 in | UL 746 B |
| Flammability, UL94 | V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | |
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | ||
| Glow Wire Test | 850 °C @Thickness 1.00 mm | 1560 °F @Thickness 0.0394 in | IEC 60695-2-1/0-3 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified |