- 密度 [g/cm3]: 1.09
- 吸水率 [%]: 0.9
- 缺口沖擊強度: 0.694
- 拉伸強度 [MPa]: 72.4
- 彎曲模量 [MPa]: 2.48
- 硬度: 108.0
- 熱變形溫度 [℃]: 45.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in3 | ASTM D792 |
| Water Absorption | 0.90 % @Time 86400 sec | 0.90 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm @Thickness 3.17 mm | 0.0080 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Break | 6.0 % | 6.0 % | ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Thickness 3.17 mm | 1.30 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 126 μm/m-°C | 70.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 45.0 °C | 113 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 23.9 °C | 75.0 °F | Unannealed; ASTM D648 |