- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 0.017
- 缺口沖擊強度: 0.214
- 拉伸強度 [MPa]: 34.0
- 斷裂伸長率 [%]: 72.4
- 彎曲強度 [MPa]: 7.5
- 彎曲模量 [MPa]: 2.76
- 硬度: 114.0
- 熱變形溫度 [℃]: 169.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 - 1.70 g/cc | 0.0405 - 0.0614 lb/in3 | Average value: 1.35 g/cc Grade Count:142 |
| Filler Content | 5.00 - 60.0 % | 5.00 - 60.0 % | Average value: 27.3 % Grade Count:100 |
| Water Absorption | 0.0170 - 2.10 % | 0.0170 - 2.10 % | Average value: 0.448 % Grade Count:94 |
| Moisture Absorption at Equilibrium | 0.100 - 1.00 % | 0.100 - 1.00 % | Average value: 0.715 % Grade Count:13 |
| Water Absorption at Saturation | 1.90 - 2.60 % | 1.90 - 2.60 % | Average value: 2.11 % Grade Count:8 |
| Additive Loading | 13.0 - 30.0 % | 13.0 - 30.0 % | Average value: 22.6 % Grade Count:5 |
| Linear Mold Shrinkage | 0.00100 - 0.0300 cm/cm | 0.00100 - 0.0300 in/in | Average value: 0.00467 cm/cm Grade Count:140 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.0120 cm/cm | 0.00200 - 0.0120 in/in | Average value: 0.00490 cm/cm Grade Count:54 |
| Linear Mold Shrinkage, Transverse | 0.00700 - 0.0170 cm/cm | 0.00700 - 0.0170 in/in | Average value: 0.0105 cm/cm Grade Count:21 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 114 - 122 | 114 - 122 | Average value: 119 Grade Count:43 |
| Ball Indentation Hardness | 145 - 220 MPa | 21000 - 31900 psi | Average value: 180 MPa Grade Count:6 |
| Tensile Strength, Ultimate | 7.50 - 200 MPa | 1090 - 29000 psi | Average value: 118 MPa Grade Count:137 |
| 75.0 - 235 MPa @Temperature -40.0 - 121 °C | 10900 - 34100 psi @Temperature -40.0 - 250 °F | Average value: 72.8 MPa Grade Count:1 | |
| 4.005 - 225.8 MPa @Temperature -40.0 - 150 °C | 580.9 - 32750 psi @Temperature -40.0 - 302 °F | Average value: 72.8 MPa Grade Count:2 | |
| 4.005 - 225.8 MPa @Strain 0.100 - 5.00 % | 580.9 - 32750 psi @Strain 0.100 - 5.00 % | Average value: 72.8 MPa Grade Count:2 | |
| Tensile Strength, Yield | 34.0 - 183 MPa | 4930 - 26500 psi | Average value: 114 MPa Grade Count:14 |
| Elongation at Break | 1.00 - 23.0 % | 1.00 - 23.0 % | Average value: 3.78 % Grade Count:139 |
| Elongation at Yield | 3.00 - 12.0 % | 3.00 - 12.0 % | Average value: 5.47 % Grade Count:8 |
| Modulus of Elasticity | 2.65 - 17.9 GPa | 384 - 2600 ksi | Average value: 8.21 GPa Grade Count:122 |
| Flexural Yield Strength | 72.4 - 303 MPa | 10500 - 44000 psi | Average value: 194 MPa Grade Count:122 |
| Flexural Modulus | 2.76 - 17.9 GPa | 400 - 2600 ksi | Average value: 7.37 GPa Grade Count:129 |
| Compressive Yield Strength | 89.6 - 179 MPa | 13000 - 26000 psi | Average value: 131 MPa Grade Count:26 |
| Shear Modulus | 0.00400 - 1.806 GPa @Temperature -50.0 - 220 °C | 0.580 - 261.9 ksi @Temperature -58.0 - 428 °F | Average value: 0.826 GPa Grade Count:1 |
| Shear Strength | 76.0 - 83.0 MPa | 11000 - 12000 psi | Average value: 78.3 MPa Grade Count:3 |
| Izod Impact, Notched | 0.214 - 1.87 J/cm | 0.401 - 3.50 ft-lb/in | Average value: 0.986 J/cm Grade Count:127 |
| Izod Impact, Unnotched | 1.33 - 16.0 J/cm | 2.50 - 30.0 ft-lb/in | Average value: 7.55 J/cm Grade Count:101 |
| Izod Impact, Notched (ISO) | 3.70 - 17.0 kJ/m2 | 1.76 - 8.09 ft-lb/in2 | Average value: 11.3 kJ/m2 Grade Count:11 |
| 10.0 - 15.0 kJ/m2 @Temperature -40.0 - -30.0 °C | 4.76 - 7.14 ft-lb/in2 @Temperature -40.0 - -22.0 °F | Average value: 11.1 kJ/m2 Grade Count:7 | |
| Izod Impact, Unnotched (ISO) | 16.0 - 78.3 kJ/m2 | 7.61 - 37.3 ft-lb/in2 | Average value: 52.6 kJ/m2 Grade Count:7 |
| 45.0 - 60.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 21.4 - 28.6 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 52.5 kJ/m2 Grade Count:3 | |
| Charpy Impact Unnotched | 4.60 - 10.4 J/cm2 | 21.9 - 49.5 ft-lb/in2 | Average value: 8.49 J/cm2 Grade Count:19 |
| 2.00 - 11.0 J/cm2 @Temperature -30.0 - 30.0 °C | 9.52 - 52.4 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 7.72 J/cm2 Grade Count:19 | |
| Charpy Impact, Notched | 0.400 - 2.00 J/cm2 | 1.90 - 9.52 ft-lb/in2 | Average value: 1.44 J/cm2 Grade Count:22 |
| 0.300 - 1.70 J/cm2 @Temperature -40.0 - 30.0 °C | 1.43 - 8.09 ft-lb/in2 @Temperature -40.0 - 86.0 °F | Average value: 1.07 J/cm2 Grade Count:22 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 1.00e+16 ohm-cm | 10.0 - 1.00e+16 ohm-cm | Average value: 2.83e+14 ohm-cm Grade Count:75 |
| Surface Resistance | 100 - 1.00e+15 ohm | 100 - 1.00e+15 ohm | Average value: 2.50e+14 ohm Grade Count:10 |
| Dielectric Constant | 3.10 - 4.40 | 3.10 - 4.40 | Average value: 3.79 Grade Count:30 |
| Dielectric Strength | 18.7 - 38.0 kV/mm | 475 - 965 kV/in | Average value: 25.0 kV/mm Grade Count:34 |
| Dissipation Factor | 0.0110 - 0.160 | 0.0110 - 0.160 | Average value: 0.0262 Grade Count:29 |
| Arc Resistance | 110 - 120 sec | 110 - 120 sec | Average value: 117 sec Grade Count:12 |
| Comparative Tracking Index | 550 - 600 V | 550 - 600 V | Average value: 597 V Grade Count:16 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 10.0 - 500 μm/m-°C | 5.56 - 278 μin/in-°F | Average value: 206 μm/m-°C Grade Count:46 |
| 500 - 500 μm/m-°C @Temperature 55.0 - 160 °C | 278 - 278 μin/in-°F @Temperature 131 - 320 °F | Average value: 500 μm/m-°C Grade Count:6 | |
| CTE, linear, Transverse to Flow | 46.8 - 113 μm/m-°C | 26.0 - 62.8 μin/in-°F | Average value: 87.6 μm/m-°C Grade Count:20 |
| 139 - 158 μm/m-°C @Temperature 55.0 - 160 °C | 77.2 - 87.8 μin/in-°F @Temperature 131 - 320 °F | Average value: 151 μm/m-°C Grade Count:6 | |
| Thermal Conductivity | 0.259 - 0.576 W/m-K | 1.80 - 4.00 BTU-in/hr-ft2-°F | Average value: 0.416 W/m-K Grade Count:23 |
| Melting Point | 212 - 224 °C | 414 - 435 °F | Average value: 216 °C Grade Count:28 |
| Maximum Service Temperature, Air | 90.0 - 180 °C | 194 - 356 °F | Average value: 143 °C Grade Count:6 |
| Deflection Temperature at 0.46 MPa (66 psi) | 169 - 225 °C | 336 - 437 °F | Average value: 212 °C Grade Count:84 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 - 218 °C | 140 - 425 °F | Average value: 199 °C Grade Count:126 |
| Deflection Temperature at 8.0 MPa | 110 - 120 °C | 230 - 248 °F | Average value: 115 °C Grade Count:6 |
| Vicat Softening Point | 193 - 210 °C | 379 - 410 °F | Average value: 202 °C Grade Count:9 |
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | Average value: 70.0 °C Grade Count:4 |
| UL RTI, Electrical | 65.0 - 120 °C | 149 - 248 °F | Average value: 98.3 °C Grade Count:6 |
| UL RTI, Mechanical without Impact | 65.0 - 120 °C | 149 - 248 °F | Average value: 96.4 °C Grade Count:6 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:116 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 252 - 279 °C | 485 - 535 °F | Average value: 266 °C Grade Count:57 |
| Melt Temperature | 218 - 300 °C | 424 - 572 °F | Average value: 266 °C Grade Count:52 |
| Mold Temperature | 60.0 - 120 °C | 140 - 248 °F | Average value: 80.2 °C Grade Count:109 |
| Drying Temperature | 79.4 - 107 °C | 175 - 225 °F | Average value: 80.2 °C Grade Count:48 |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | Average value: 3.83 hour Grade Count:41 |
| 2.00 - 4.00 hour @Temperature 79.4 - 79.4 °C | 2.00 - 4.00 hour @Temperature 175 - 175 °F | Average value: 3.00 hour Grade Count:3 | |
| Moisture Content | 0.0200 - 0.200 % | 0.0200 - 0.200 % | Average value: 0.188 % Grade Count:44 |
| Dew Point | -17.8 °C | 0.000 °F | Average value: -17.8 °C Grade Count:36 |
| Injection Pressure | 4.96 - 130 MPa | 720 - 18900 psi | Average value: 89.7 MPa Grade Count:98 |
| Back Pressure | 0.172 - 0.517 MPa | 24.9 - 75.0 psi | Average value: 0.316 MPa Grade Count:6 |
| Shot Size | 30.0 - 80.0 % | 30.0 - 80.0 % | Average value: 55.0 % Grade Count:4 |
| Screw Speed | 20.0 - 100 rpm | 20.0 - 100 rpm | Average value: 60.0 rpm Grade Count:4 |